i have herd that the Tig om CM process is acceptable if you wrap the weld and let it cool slowly???? not that any one does it.
i think in reality to make it PERFECT you would want to heat treat the entire cage after welding, but no one is going to do that.
DOM is definatly cheaper. and the fit is not quite as critical and it can then be mig welded..
Deuce454 i know the procees is different but tig and gas welding would be esentially the same? no just that tig would be more controlable would it not?
and what is the BEST filler to use on CM if anyone can shed some light there, we use a 312 rod. only because no one sems to know what if anything is better. my fab guy has been building roadrace cars for 15 years and that is the best material he has found to date.
|